Gnee Steel (Tianjin) Co., Ltd. is one of the most reliable manufacturers and suppliers of en 10025-2 grade s355j2c in China. Welcome to wholesale customized en 10025-2 grade s355j2c at low price from our factory. If you have any enquiry about free sample and cheap products, please feel free to email us.
Properties
General
| Property | Value | Comment |
|---|---|---|
|
Density
|
7.8 - 7.9 g/cm³
|
Typical for Low Carbon Steel |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
|
Elastic modulus
|
200 - 215 GPa
|
Typical for Low Carbon Steel |
||||
|
Elongation
|
17.7 %
|
Predicted Value, A200 |
||||
|
22 %
|
Predicted Value, A5 |
|||||
|
23.4 %
|
Predicted Value, A50 |
|||||
|
20 °C |
12 %
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
A80 Transverse |
|
|
20 °C |
13 %
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
A80 Transverse |
|
|
20 °C |
14 %
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
A80 Transverse |
|
|
20 °C |
14 %
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
A80 |
|
|
20 °C |
15 %
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
A80 Transverse |
|
|
20 °C |
15 %
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
A80 |
|
|
20 °C |
16 %
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
A80 Transverse |
|
|
20 °C |
16 %
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
A80 |
|
|
20 °C |
17 %
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
A80 |
|
|
20 °C |
17 %
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
Transverse |
|
|
20 °C |
17 %
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
||
|
20 °C |
18 %
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
A80 |
|
|
20 °C |
18 %
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
Transverse |
|
|
20 °C |
18 %
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
||
|
20 °C |
19 %
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
Transverse |
|
|
20 °C |
20 %
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
Transverse |
|
|
20 °C |
20 %
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
||
|
20 °C |
21 %
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
||
|
20 °C |
22 %
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
||
|
Poisson's ratio
|
0.29 [-]
|
Typical for Low Carbon Steel |
||||
|
Reduction of area |
43.6 %
|
Predicted Value, Transverse |
||||
|
52.3 %
|
Predicted Value |
|||||
|
Shear modulus
|
82 GPa
|
Typical for Low Carbon Steel |
||||
|
Shear strength |
522.6 MPa
|
Predicted Value |
||||
|
Tensile strength
|
20 °C |
450 - 680 MPa
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
|
|
20 °C |
450 - 630 MPa
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
||
|
20 °C |
450 - 600 MPa
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
||
|
20 °C |
470 - 680 MPa
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
||
|
20 °C |
470 - 630 MPa
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
||
|
20 °C |
470 - 600 MPa
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
||
|
20 °C |
510 - 680 MPa
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
||
|
20 °C |
510 - 630 MPa
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
||
|
20 °C |
510 - 600 MPa
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
||
|
Yield strength
|
255.8 MPa
|
Predicted Value, RP1 |
||||
|
318.4 MPa
|
Predicted Value, RP1 Transverse |
|||||
|
346.1 MPa
|
Predicted Value, Transverse |
|||||
|
379.5 MPa
|
Predicted Value, RP05 |
|||||
|
429.7 MPa
|
Predicted Value, RP02 |
|||||
|
480.2 MPa
|
Predicted Value, RP02 Transverse |
|||||
|
482.8 MPa
|
Predicted Value, RP002 |
|||||
|
20 °C |
265 MPa
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
||
|
20 °C |
275 MPa
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
||
|
20 °C |
285 MPa
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
||
|
20 °C |
295 MPa
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
||
|
20 °C |
315 MPa
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
||
|
20 °C |
325 MPa
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
||
|
20 °C |
335 MPa
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
||
|
20 °C |
345 MPa
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
||
|
20 °C |
355 MPa
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
Thermal
| Property | Value | Comment |
|---|---|---|
|
Coefficient of thermal expansion
|
1.32e-05 - 1.38e-05 1/K
|
Typical for Low Carbon Steel |
|
Max service temperature |
317.8 °C
|
Predicted Value, Long |
|
500 °C
|
Typical for Carbon Steel |
|
|
Melting point
|
1480 - 1526 °C
|
Typical for Low Carbon Steel |
|
Specific heat capacity
|
465 J/(kg·K)
|
Typical for Low Carbon Steel |
|
Thermal conductivity
|
25 - 93 W/(m·K)
|
Typical for Low Carbon Steel |
Electrical
| Property | Value | Comment |
|---|---|---|
|
Electrical conductivity
|
7 S/m
|
Predicted Value |
|
Electrical resistivity
|
1.43e-07 - 1.74e-07 Ω·m
|
Typical for Carbon Steel |
Magnetic
| Property | Value | Comment |
|---|---|---|
|
Curie temperature |
770 °C
|
Typical for Low Carbon Steel |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
|
Carbon |
0.2 %
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
|
Copper |
0.55 %
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
|
Manganese |
1.6 %
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
|
Phosphorus |
0.025 %
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
|
Silicon |
0.55 %
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
|
Sulfur |
0.025 %
|
normalized or normalized formed (+N) |
EN 10025-2, EN 10025 |
Strip, Sheet, Flat, Rod, Wire |
Hot Tags: EN 10025-2 Grade S355J2C, China EN 10025-2 Grade S355J2C manufacturers, suppliers, factory, 201 Plate Cold Rolled Steel Sheet, cold rolled steel for remanufacturing, cold rolled steel for eco friendly projects, cold rolled steel for business transformation, cold rolled steel for research and development, cold rolled steel for international standards